Resin Flooring System Resuflor™ Industry HCS

Name: Resin Flooring System Resuflor™ Industry HCS
Brand: Sherwin-Williams
SKU: 2u5ZRYidUv313fHDorqVxd

Verified by manufacturer 4 months ago

Sherwin-Williams

High compressive strength epoxy screed flooring system.

Jump to:

+44 (0)1204 521771 Website

Application

For use in:

Heavy traffic buildings with high loads.
Military facilities
Heavy manufacturing
Aerospace manufacturing
Paper mills
Pharmaceutical areas.
Animal compounds and veterinary areas.
Production areas.
Industrial workshops.
Prisons and police cells.

Description

Resuflor Industry HCS is a heavy duty epoxy flooring system for industrial floors with high compressive strength. The floor is able to withstand aggressive cleaning processes such as steam and hot water.

The system is typically applied at 6–9 mm thickness using aggregates which are free of crystalline silica promoting a more environmentally friendly product with less dust than traditional epoxy resin screeds. Whilst an impervious finish can be achieved with Resuflor Industry HCS a seal coat can be applied to enhance ease of cleaning. Resuflor Industry HCS can be used to form coving, ramps and concrete surface repairs where required.

Features and benefits:

Hard wearing functional surface.
Very high compressive strength - 114N/mm2
Silk or matt finish
Can be used for coving.
Seamless floor to coving finish.
Ease of application.
Low odour.
Good slip resistance *can be increased with added aggregates
High abrasion and impact resistance.
Good chemical resistance.
FerFa class: 6.
Will accept light traffic after 12 hours.

General information

Color	Grey Beige Black Blue Brown Cream Yellow Orange Green Red Ivory Purple White Show more
Finish	Smooth
Material	Epoxy resin Silica Aggregate
Shape	Formless
Length	Bespoke
Width	Bespoke
Height	6 mm Manufacturer guidance 6–9 mm.

Uniclass	Ss_30_42_54_75 Resin flooring systemsPrimary
CAWS	M12/110 Resin flooring M12/10 Resin flooring

Specification data - Resin flooring systems

Substrate	-
Testing	Moisture content to BS 8204.
Preparation	Preparation of existing substrates. Guidance for specification option: Substrates must be clean, sound, dry and free of surface laitance with a minimum strength of 25 N/mm². Mechanically prepare substrate to provide a surface texture that will function as a key for the resin. Remove all dust and debris. Repair significant mechanical damage, pitting and cracks.
Levelling screed	Resuflor Screed HCS.
Primer	Resuprime ST.
Surface treatment	Resupen WB.

Shore Hardness - D	To BS ISO 7619-1:2010, 84 (at 24 hours).
Abrasion resistance	To BS EN 13892-4:2002, AR 0.5.
CompressiveStrength	To BS EN 13892-2:2002, 114 N/mm².
TensileStrength	To BS 6319-7:1985, 8.6 N/mm².
Flexural strength	To BS EN ISO 178:2010+A1:2013, 3.2 N/mm².
Bond strength	To BS EN 13892-8:2002, >3 N/mm².
Impact resistance	To BS EN 1504-2:2004, Class II.
Temperature resistance	Up to 45°C.
Application temperature	10–25ºC.
Reaction to fire	To BS EN 13501-1:2018, Bfl–s1.
System thickness	6–9 mm.